Polyethylene
Polyethylene
You can review the product details and features below.

High-Density Polyethylene Specification (granulated)

TDS(State Turkmenistan Standart Service)-1097-2018

Mark - A4009MFN1325

Melt flow rate, (2.16 kg), g/10min

0.7-1,1

Density kg/m3

958-962

Tensile yield strength, at 50 mm/min, Mpa

27

Tensile elongation at yield, at 50 mm/min, Mpa

19

Elongation at break %

500

Flexural modulus (1% secant), at

1.4mm/min, Mpa

1000

High-Density Polyethylene Specification (granulated)

TDS(State Turkmenistan Standart Service)-1097-2018

Mark - B50-35H-111

Melt flow rate, (2.16 kg) g/10min

0,3-0,4

Density kg/m3

948-952

Tensile yield strength, at 2 inch/min, Mpa

21

Tensile elongation at yield, %

500

Flexural modulus (1% secant), at 1.4 mm/min, Mpa

900

Heat resisitance on Vicka , °C

120

Bell Telephone thermal testing on the breakdown voltage , resistance to cracking when the voltage, at 50 °C

30 h

High-Density Polyethylene Specification (granulated)

TDS(State Turkmenistan Standart Service)-1097-2018

Mark - HP50-25-155

Melt flow rate, (2.16 kg), g/10min

0,18-0,26

Density, kg/m3

949-953

Tensile yield strength, (2 inch/min) , Mpa

22

Tensile elongation at yield, %

700

Heat resistance on Vicka , Mpa

120

Flexural modulus, Mpa

900

High-Density Polyethylene Specification (granulated)

TDS(State Turkmenistan Standart Service)-1097-2018

Mark - J53-08 N2000

Melt flow rate, (21.6 kg), g/10min

6,5-9,5

Density 23 °C, kg/m3

951-955

Tensile strength at yield longitudinal direction, Mpa

27

Tensile strength at yield in transverse direction, Mpa

25

Tensile strength at break in the longitudinal direction, Mpa

66

Tensile at break in the longitudinal / tranverse direction, %

> 250 / >350

Impact strength, g/10 min

250

High-Density Polyethylene Specification (granulated)

TDS(State Turkmenistan Standart Service)-1097-2018

Mark - T50-500

Melt flow rate, (2.16 kg) , g/10min

5,4-7,6

Density, kg/m3

951-955

Tensile yield strength, Mpa

24

Tensile elongation at yield, %

800

Flexural modulus ( 1 mm/min ), Mpa

900

Notched izod under load, J/m

57

Heat resisitance on Vicka, °C

120

High-Density Polyethylene Specification (granulated)

TDS(State Turkmenistan Standart Service)-1097-2018

Mark - T60-475-119

Melt flow rate, (2.16 kg) , g/10min

4 -5,6

Density, kg/m3

959-963

Tensile yield strength, Mpa

28

Notched izod under load, J/m

55

Flexural modulus ( 1 mm/min ), Mpa

1250

Heat resisitance on Vicka

120 °C

High-Density Polyethylene Specification (granulated)
TDS(State Turkmenistan Standart Service)-1097-2018
Mark - INpipe 100

Melt flow rate, (2.16 kg), g/10min

0,25-0,35

Density, kg/m3

957-961

Tensile yield strength, at 2 inch/min, Mpa

21

Tensile elongation at yield, %

600

Heat resisitance on Vicka, °C

120

Bell Telephone thermal testing on the breakdown voltage , resistance to cracking when the voltage, at 50 °C

1000 h