Polypropylene

Polypropylene

You can review the product details and features below.

Mark - LH5072-03.O

Melt flow rate, (230°C / 2.16g), g/10 min	3,0-4,0
Density, kg/sm³	0.90-0,91
Tensile yield strength, at 50 mm/min, MPa	33
Tensile elongation at yield, at 50 mm/min, %	7,6
Flexural modulus (1% secant), at 1.3 mm/min, MPa	1275
Notched Izod impact strength, at 23°C, J/m	30

Mark - L R7175-35.P

Melt flow rate, (230°C / 2.16g) g/10 min	30,0-40,0
Density, kg/sm³	0.885-0,905
Tensile yield strength, at 50 mm/min, MPa	25
Tensile elongation at yield, at 50 mm/min, %	7,6
Flexural modulus (1% secant), at 1.4 mm/min, MPa	935
Notched Izod impact strength, at 23°C, J/m	29

Mark - L H3150-02.0

PROPERTY	SI units
Melt flow rate, (230°C / 2.16 kg), kg/ 10min)	2,1-2,9
Density, kg/sm³	0.90-0,91
Tensile yield strength, at 50 mm/min, MPa	32 MPa
Tensile elongation at yield, at 50 mm/min, %	7,6
Flexural modulus (1% secant), at 1.4 mm/min, MPa	1360
Notched Izod impact strength, at 23°C, J/m	34 J/m

Melt flow rate, (230°C / 2.16g), g/10min	21,0-29,0
Density, kg/sm3	0.90-0,91
Tensile yield strength, at 50 mm/min, MPa	33
Tensile elongation at yield, at 50 mm/min, %	6,6
Flexural modulus (1% secant), at 1.4 mm/min, MPa	1258
Notched Izod impact strength, at 23°C, J/m	18

TURKMENPLEN (POLYPROPYLEN)

T$ 05766698-20-2007

X«	Description of Index	Figure
X«	Description of Index	TPP D30 S	TPP F 79 FB	TPP D 382 BF
1	Volume speed of fluidity, g/10 min	2,7-3,7	10-15	2,7-3,7
2	Index of polymeric granules turning yellow, not more than	2	2	2
3	Dimension of granules, ps/g	40-60	40-60	40-60
4	Uniformity of granules,%, not more than	50	50	50
5	The elasticity module at a bend, N/mm", not less than	1300	1450	1300
6	Strength at a stretching in a fluidity limit, N/mm*, not less than	30	31	30
7	Relative lengthening at a stretching in a fluidity limit, %, not less than	11	12	11
8	Shock durabilityby khojy (with a cut at 23°C), kDj/m²	4,5	2,5	4,5
9	Softening temperature by Vick (ION),°C, not less than	145	150
10	Temperature of admissible deformation at 0,46 MPa, °C, not less than	110	130
11	Thermooxidizing stability at 150°C (in the environment of air), hour, not less than	360	120	360
12	Definition of number and the sizes of gels in polyolefines, not more than Defects >0,2 mm Defects 0,7-1,5 mm Defects 1,5-2,5 mm Defects > 2,5 mm	-	-	500 50 10 0
13	Turbidity polyolefine plates and films			No standard, determination necessary

TURKMENPLEN (POLYPROPYLEN)

T$ 05766698-20-2007

X«	Description of Index	Figure
X«	Description of Index	TPP D30 S	TPP F 79 FB	TPP D 382 BF
1	Volume speed of fluidity, g/10 min	2,7-3,7	10-15	2,7-3,7
2	Index of polymeric granules turning yellow, not more than	2	2	2
3	Dimension of granules, ps/g	40-60	40-60	40-60
4	Uniformity of granules,%, not more than	50	50	50
5	The elasticity module at a bend, N/mm", not less than	1300	1450	1300
6	Strength at a stretching in a fluidity limit, N/mm*, not less than	30	31	30
7	Relative lengthening at a stretching in a fluidity limit, %, not less than	11	12	11
8	Shock durabilityby khojy (with a cut at 23°C), kDj/m²	4,5	2,5	4,5
9	Softening temperature by Vick (ION),°C, not less than	145	150
10	Temperature of admissible deformation at 0,46 MPa, °C, not less than	110	130
11	Thermooxidizing stability at 150°C (in the environment of air), hour, not less than	360	120	360
12	Definition of number and the sizes of gels in polyolefines, not more than Defects >0,2 mm Defects 0,7-1,5 mm Defects 1,5-2,5 mm Defects > 2,5 mm	-	-	500 50 10 0
13	Turbidity polyolefine plates and films			No standard, determination necessary

SC « Turkmengas»
Polypropylene Specification
TDS(State Turkmenistan Standart Service)-1098-2018
Mark - LH3066-03.0

PROPERTY	SI units
Melt flow rate, (230°C /2.16g), g/lOmin	2,9-3,9
Density, kg/sm’	0.90-0,91
Tensile yield strength, at 50 mm/min, MPa	29
Tensile elongation at yield, at 50 mm/min, %	8,6
Flexural modulus (1% secant), at 1.4 mm/min, MPa	1190 MPa
Notched Izod impact strength, at 23°C, J/m	34

TURKMENPLEN (POLYPROPYLEN)

T$ 05766698-20-2007

X«	Description of Index	Figure
X«	Description of Index	TPP D30 S	TPP F 79 FB	TPP D 382 BF
1	Volume speed of fluidity, g/10 min	2,7-3,7	10-15	2,7-3,7
2	Index of polymeric granules turning yellow, not more than	2	2	2
3	Dimension of granules, ps/g	40-60	40-60	40-60
4	Uniformity of granules,%, not more than	50	50	50
5	The elasticity module at a bend, N/mm", not less than	1300	1450	1300
6	Strength at a stretching in a fluidity limit, N/mm*, not less than	30	31	30
7	Relative lengthening at a stretching in a fluidity limit, %, not less than	11	12	11
8	Shock durabilityby khojy (with a cut at 23°C), kDj/m²	4,5	2,5	4,5
9	Softening temperature by Vick (ION),°C, not less than	145	150
10	Temperature of admissible deformation at 0,46 MPa, °C, not less than	110	130
11	Thermooxidizing stability at 150°C (in the environment of air), hour, not less than	360	120	360
12	Definition of number and the sizes of gels in polyolefines, not more than Defects >0,2 mm Defects 0,7-1,5 mm Defects 1,5-2,5 mm Defects > 2,5 mm	-	-	500 50 10 0
13	Turbidity polyolefine plates and films			No standard, determination necessary